| 標準 | GB12771-2000 | HG20537.2-92 | HG20537.3-92 | HG20537.4-92 | ASTM A312/A312M | ASTM A249/A249M | ASTM A688/A688M | JISG3468 | |||||||||||||||
| 項目 | |||||||||||||||||||||||
| 牌號 | 0Cr19Ni9
00Cr19Ni10 0Cr17Ni12Mo2 00Cr17Ni14Mo2 0Cr18Ni10Ti (1Cr18Ni9Ti) |
0Cr18Ni9
00Cr19Ni10 0Cr17Ni12Mo2 00Cr17Ni14Mo2 0Cr18Ni10Ti (1Cr18Ni9Ti) |
0Cr18Ni9
00Cr19Ni10 0Cr17Ni12Mo2 00Cr17Ni14Mo2 0Cr18Ni10Ti (1Cr18Ni9Ti) |
0Cr18Ni9
00Cr19Ni10 0Cr17Ni12Mo2 00Cr17Ni14Mo2 0Cr18Ni10Ti (1Cr18Ni9Ti) |
TP304 TP304L
TP316 TP316L TP321 |
TP304 TP304L
TP316 TP316L TP321 |
TP304 TP304L TP304N
TP316 TP316N TP316L TP304LN TP316LN |
SUS304TPY
SUS304LTPY SUS316TPY SUS316LTPY SUS321TPY |
|||||||||||||||
| 規格範圍(mm) | D<=630 | 10<=D<=76 | D<=325 | 377<=D<=1020 | 10.3<=D<=762 | D<=127 0.4<=t<=8.1 | 15.9<d<=25.4 75<=D<=1200或更大t>=0.7 | 165.2<=D<=1016 | |||||||||||||||
| 屈服強度ó0.2(Mpa) | >=180;>=210 | >=175;>=205 | >=175;>=205 | >=175;>=205 | <=170;>=205 | >=170;>=215 | >=175;>=205;>=240 | >=175;>=205 | |||||||||||||||
| 抗拉強度ób(Mpa) | >=480;>=520 | >=480;>=520 | >=480;>=520 | >=480;>=520 | >=485;>=515 | >=485;>=515 | >=485;>=515;>=550 | >=480;>=520 | |||||||||||||||
| 延伸率§5(%) | >=35(焊態>=25) | >=40 | >=40 | >=40 | >=35 | >=35 | >=35 | >=35(橫向>=25) | |||||||||||||||
| 焊縫橫向彎曲或展平 | 展平D>=200弦高H=D/4 | 反向展平 | - | 正彎、反彎、彎芯直徑d=3t | 焊縫橫嚮導面彎曲ASTM370 | 反向彎曲(d=4t)或展平 | 同左 | 特殊要求JISZ3122 | |||||||||||||||
| 壓扁試驗(mm) | D<200 H=D/3 | H=1.09t/(0.09+t/D) | H=1.09t/(0.09+t/D) | - | - | H=1.09t/(0.09+t/D)並試驗完好性 | - | - | |||||||||||||||
| 擴口、卷邊 | - | a=60° 擴20%D | - | - | - | 卷邊寬度15%D | 卷邊寬度15%D | - | |||||||||||||||
| 無損探傷 | - | GB/T7735 B級 | GB/T 7735 A級當t>6.3mm時應達到GB3323III級(20%) | GB3323 100%x射線II級
20%x射線III級 |
補充要求(射線探傷) | 代替水壓 | 補充要求(渦流探傷) | 特殊要求JISZ3106 | |||||||||||||||
| 壓力試驗(Mpa) | 水壓 | Pmax=10可用渦流探傷代替GB/T7735A級 | 雙方協議可用無損探傷代替
P=2Rt/D 式中R=50% ó0.2Pmax=7.5 |
1.5-6.0按壁厚系列分或經雙方協議用無損探傷代替Pmax=2Rt/D式中R=50%ó0.2 | 1.5-2.5按壁厚系列分或經雙方協議用縫縫探傷代替 | ASTM A530/A530M
D<=270 P=2Rt/D式中R=50%ó0.2 |
可用無損探傷代替 | ASTM A450/A450M | 1.5-2.5按壁厚系列分 | ||||||||||||||
| 氣壓 | - | P=1MPa | |||||||||||||||||||||
| 晶腐試驗 | GB4334.5 | 附加要求GB4334.5 | 附加要求GB4334.5 | 附加要求GB4334.5 | ASTM A262E法(補充要求) | ASTM A262E法(補充要求) | ASTM A262E法(補充要求) | - | |||||||||||||||
| 熱處理 | 要求 | 要求 | 要求 | 附加要求 | 要求 | 要求 | 要求 | 特殊要求 | |||||||||||||||
| I級 | II級 | ||||||||||||||||||||||
| 外徑偏差(mm) | 焊
態 |
外徑 | 普通 | 高級 | 外徑 | 允許偏差 | 外徑 | 允許偏差 | 外徑 | 允許偏差 | ±1%D(D按周長測算) | 外徑 | 允許偏差 | 外徑 | 允許偏差 | 外徑 | 允許偏差 | 外徑 | 允許偏差 | ||||
| <20 | ±0.30 | ±0.20 | <25 | ±0.10 | <=10 | ±0.15 | <=168 | ±0.75%D最小值為±0.3 | 10.3-48.3 | +0.40/-0.80 | <25.4 | ±0.10 | <25.4 | ±0.10 | <=318.5 | ±1%D | |||||||
| >=20-<50 | ±0.50 | ±0.40 | 25-38 | ±0.15 | >10-30 | ±0.20 | >48.3-114.3 | +0.80/-0.80 | 25.4~<=38.1 | ±0.15 | 25.4~<=38.1 | ±0.15 | - | - | |||||||||
| >=50 | ±1%D | ±0.80%D | >38-<51 | ±0.20 | >30-50 | ±0.30 | >114.3-219.1 | +1.60/-0.80 | >38.1~<50.8 | ±0.20 | >38.1~<50.8 | ±0.20 | - | - | |||||||||
| 固溶態 | <13 | ±0.25 | ±0.20 | 51-63 | ±0.25 | >50 | ±0.8%D | >219.1-457.2 | +2.40/-0.80 | 50.8~<63.5 | ±0.25 | 50.8~<63.5 | ±0.25 | - | - | ||||||||
| >=13-<25 | ±0.40 | ±0.30 | >=63-76 | ±0.30 | - | - | >457.2-660.4 | +3.20/-0.80 | 63.5~<76.2 | ±0.30 | 63.5~<76.2 | ±0.30 | >318.5 | ±0.5%D | |||||||||
| >=25-<40 | ±0.60 | ±0.40 | - | >168-325 | ±1%D | >660.4-864 | +4.00/-0.80 | 76.2~<=101.6 | ±0.38 | 76.2~<=101.6 | ±0.38 | - | - | ||||||||||
| >=40-<65 | ±0.80 | ±0.60 | >864-1219.2 | +4.80/-0.80 | >101.6~<=190.5 | +0.38/-0.64 | >101.6~<=190.5 | +0.38/-0.64 | - | - | |||||||||||||
| >=65-<90 | ±1.00 | ±0.80 | - | >190.5~<=228.6 | +0.38-1.14 | >190.5~<=228.6 | +0.38-1.14 | - | - | ||||||||||||||
| >=90-<140 | ±1.20 | ±1.00 | - | - | - | - | - | - | |||||||||||||||
| >=140-<300 | ±1.5%D | ±1.0%D | - | - | - | - | - | - | |||||||||||||||
| >=300-<500 | ±1.0%D | ±0.8%D | - | - | - | - | - | - | |||||||||||||||
| >=500 | 按協議 | 按協議 | - | - | - | - | - | - | |||||||||||||||
| 壁厚偏差(mm) | 壁厚 | 允許偏差 | ±0.10%t,最小允許偏差為±0.2，可雙方協議為+18%t/D | ±0.10%t,最小允許偏差為±0.2 | D<=508 | t<=8 | +15%t/-12.5%t | ±不規定/-12.5%t | ±10%t | 平均壁厚允許偏差±10%t
最小壁厚允許偏差±20%/D |
D<=508 | t<8 | +15%t/-12.5%t | ||||||||||
| t>8 | +15%t/-10%t | ||||||||||||||||||||||
| <=4 | ±0.5/-0.6 | D>508 | t<=8 | +不定%t/-12.5%t | t>=8 | +15%t/-10%t | |||||||||||||||||
| >4 | ±10%S | t>8 | +不定%t/-10%t | D>=558.8 | t<8 | +不定%t/-12.5%t | |||||||||||||||||
| t>=8 | +不定%t/-10%t | ||||||||||||||||||||||
| 不圓度偏差 | - | 同外徑偏差 | 同外徑偏差 | <=1.5%D | <=1.5%D | - | - | - | |||||||||||||||
| 彎曲度(mm/m) | 2.0mm/m~2.5mm/m | 1.0mm/m | 3.0mm/3m | 5mm/3m | 合理的直度 | 0.8mm/900mm | - | 實用性平直 | |||||||||||||||
| 焊縫余高(mm) | 不超過1.5mm | 外縫余高與母材平
內縫余高D<20 <=0.15;D>=20 <=0.25 |
外縫余高與母材平
內縫余高<=15%t |
內縫余高<=25%t且<=3
外縫余高<=50%t且<=3 |
- | - | - | 特殊要求內縫余高<=1.5
外縫余高<=3.0 |
|||||||||||||||
| 其他要求 | - | HRB<90 | - | - | HRB<=90 | HRB<=90 | HRB<=90 | - | |||||||||||||||
ASTM不鏽鋼標準—鋼管
ASTM A213 無縫鐵素體和奧氏體合金鋼鍋爐、過熱器和換熱器管
ASTM A249 鍋爐、過熱器、換熱器和冷凝器用焊接奧氏體鋼管
ASTM A268/A268M-10 一般用鐵素體和馬氏體不鏽鋼無縫和焊接鋼管
ASTM A269 -10 一般用途無縫和焊接奧氏體不鏽鋼管
ASTM A270/A270M-10 衛生設備用無縫和焊接奧氏體不鏽鋼
ASTM A312/A312M-09 無縫、焊接和冷加工用奧氏體不鏽鋼管
ASTM A358 高溫用電熔焊奧氏體鉻鎳合金鋼管
ASTM A381 高壓輸送用金屬弧焊鋼管
ASTM A409 腐蝕場所或高溫下使用的焊接大口徑奧氏體鋼管
ASTM A688/A688M-10 給水加熱器用奧氏體不鏽鋼焊管
ASTM A733-03(2009)e1 碳素鋼和奧氏體不鏽鋼焊接和無縫螺紋鋼管
ASTM A778 焊接未退火的奧氏體不鏽鋼管形制品
ASTM A789/A789M-10 一般用途無縫和焊接鐵素體/奧氏體不鏽鋼管
ASTM A790/A790M-09a 無縫與焊接鐵素體/奧氏體不鏽鋼管
ASTM A791 不退火鐵素體焊接不鏽鋼管
ASTM A803 焊接鐵素體不鏽鋼給水加熱器管
ASTM A813 單或雙焊接奧氏體不鏽鋼管
ASTM A814/A814M-08 冷加工焊接奧氏體不鏽鋼管
ASTM A826/A826M-95 增殖反應堆堆芯部件用奧氏體和鐵素體不鏽鋼管
ASTM A872/A872M-07a 腐蝕環境下用離心鑄造鐵素體/奧氏體不鏽鋼管
ASTM A928/A928M-09a 填充金屬電熔焊鐵素體/奧氏體不鏽鋼管
ASTM A999/A999M-04a(2009) 合金鋼及不鏽鋼管一般要求
ASTM A1016/A1016M -08 鐵素體和奧氏體不鏽鋼管的一般要求
結構用不鏽鋼管
ASTM A511/A511M-08 機械工程用不鏽鋼無縫管
ASTM A554 焊接不鏽鋼機械管（圓形，方矩形，橢圓型）
ASTM A632-04(2009) 一般設備用無縫和焊接奧氏體不鏽鋼管(小直徑)
ASTM A908 不鏽鋼針管
材質：304,304L,316,316L,409D,321,2205,2507,S31803.